Flexural strength, fracture toughness and fatigue crack growth behaviour of chromium alloyed γ-base TiAl

R. Gnanamoorthy, Y. Mutoh, N. Masahashi, Y. Mizuhara, M. Matsuo

研究成果: Article査読

7 被引用数 (Scopus)

抄録

Mechanical properties of γ-base titanium aluminides strongly depend on microstructural parameters. Flexural strength, fracture toughness and fatigue crack growth properties were estimated for the cast and heat-treated (HT-TiAlCr) and cast, heat treated and isothermal forged (ITF-TiAlCr) chromium alloyed γ-base titanium aluminides at room temperature. HT-TiAlCr possessed superior fracture properties compared to ITF-TiAlCr. Toughening due to microcracks, and crack bridging by uncracked ligaments were observed in the test materials. Presence of lamellar grains in HT-TiAlCr increased the crack growth resistance and contributed positively to fracture properties. The coarse grain size promoted large crack deflection and fracture surface mismatch and caused high levels of crack closure in HT-TiAlCr. Combined crack-tip blunting and bridging by ductile β-phase was significant in the case of ITF-TiAlCr. Fracture mechanisms of test materials were investigated and correlated to the fracture properties.

本文言語English
ページ(範囲)5199-5206
ページ数8
ジャーナルJournal of Materials Science
29
19
DOI
出版ステータスPublished - 1994 10月 1
外部発表はい

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Flexural strength, fracture toughness and fatigue crack growth behaviour of chromium alloyed γ-base TiAl」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル