Ferromagnetic resonance in epitaxial α + ′-martensite Fe-N films

Osamu Kohmoto, Satoshi Okamoto, Osamu Kitakami, Yutaka Shimada, Takeshi Tsuda

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Ferromagnetic resonance at 35 GHz was studied in 200-Å-thick single-crystal α + ′-martensite Fe90N10 (001) films grown on (001) GaAs substrates. From the resonance fields in both (001) basal and (100) vertical planes and the saturation magnetization (4πM) value of 23.0 kG, a large uniaxial anisotropy (Ku) along the [001] axis of 6.36 × 106 erg/cm3, a cubic anisotropy (K1) of 2.2 × 105 erg/cm3 and the gyromagnetic ratio (g-value) of 2.07 have been determined.

本文言語English
ページ(範囲)4305-4306
ページ数2
ジャーナルJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
36
7 A
出版ステータスPublished - 1997 7 1