Fe-rich Fe-Si-B-P-Cu powder cores for high-frequency power electronic applications

研究成果: Article査読

10 被引用数 (Scopus)

抄録

The Fe-rich Fe83.3Si4B8P4Cu0.7 magnetic powder with the particle size below 150 μm was obtained by spinning water atomization process. The as-prepared powder shows almost amorphous structure. The toroidal cores with outer diameter 13 mm and inner diameter 8 mm with height ∼ 4-6 mm were compacted and sintered at different temperature by spark plasma sintering technique under the maximum load of ∼ 800 MPa. High relative density (with respect to nanocrystalline ribbons of the same composition) up to ∼ 89% was obtained. The powder particles in the sintered core consist of nanocrystalline α Fe grains in the amorphous matrix. A constant initial permeability μi more than 50 was obtained up to the frequency range of 50 MHz. As expected, the permeability was found to increase with the increase in density of the core (maximum initial permeability of 364). Low magnetic coercivity Hc can be obtained in these cores, closed to ∼ 80 A/m. Lowcore loss W is due to reduced eddy-current loss (at high frequencies), resulting from the electrical insulation of the powder particles by resin. Our soft magnetic powder cores (PCs) exhibit lower core loss than the Somaloy PCs measured under a relatively high magnetic induction, e.g., 0.5 and 1 T, which may fill the gaps in high-frequency high induction application of ferrite materials.

本文言語English
論文番号6971603
ジャーナルIEEE Transactions on Magnetics
50
11
DOI
出版ステータスPublished - 2014 11 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 電子工学および電気工学

フィンガープリント

「Fe-rich Fe-Si-B-P-Cu powder cores for high-frequency power electronic applications」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル