Fatigue behavior of Fe-Cr-Ni-based metastable austenitic steels with an identical tensile strength and different solute carbon contents

Takuro Ogawa, Motomichi Koyama, Yuri Nishikura, Kaneaki Tsuzaki, Hiroshi Noguchi

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Fatigue properties of Fe-19Cr-8Ni-0.05C and Fe-19Cr-8Ni-0.14C steels were investigated using a rotating bending fatigue test machine. Fatigue limit of both of the steels were dominated by critical stress amplitude for crack initiation. Because of the austenite stability, the fatigue limit of the Fe-19Cr-8Ni-0.05C steel was 200 MPa higher than that of the Fe-19Cr-8Ni-0.14C steel. Although occurrence of dynamic strain aging in the Fe-19Cr-8Ni-0.14C was expected to improve fatigue limit, the effect did not appear due to the remarkable increase of phase stability that deteriorates positive effects of transformation-induced plasticity and transformation-induced crack closure.

本文言語English
ページ(範囲)88-97
ページ数10
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
104
2
DOI
出版ステータスPublished - 2018

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Fatigue behavior of Fe-Cr-Ni-based metastable austenitic steels with an identical tensile strength and different solute carbon contents」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル