Fabrication of YAG-SiC nanocomposites by spark plasma sintering

Lian Gao, Hongzhi Wang, Hirokazu Kawaoka, Tohru Sekino, Koichi Niihara

研究成果: Article

44 引用 (Scopus)

抜粋

The heterogeneous precipitation method was used to prepare YAG-5 vol.% SiC powder. Hot-press sintering and spark plasma sintering were used to obtain dense sintered bodies. The present results revealed that nanoscale-sized SiC particles were well distributed within the composites, with most of the particles located within the YAG grains. The bending strength of spark-plasma-sintered YAG-5 vol.% SiC nanocomposites was 565 MPa, much higher than that of monolithic YAG ceramics. The fracture mode of the YAG-5 vol.% SiC nanocomposites was transgranular. The present results indicate that YAG-5% SiC nanocomposites are good high-temperature structural materials and that spark plasma sintering is appropriate for fabricating high-performance YAG-5 vol.% SiC nanocomposites with a fine microstructure because the method involves a low sintering temperature.

元の言語English
ページ(範囲)785-789
ページ数5
ジャーナルJournal of the European Ceramic Society
22
発行部数5
DOI
出版物ステータスPublished - 2002 5

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント Fabrication of YAG-SiC nanocomposites by spark plasma sintering' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用