Fabrication of anodic porous alumina via anodizing in cyclic oxocarbon acids

Tatsuya Kikuchi, Daiki Nakajima, Jun Kawashima, Shungo Natsui, Ryosuke O. Suzuki

研究成果: Article査読

40 被引用数 (Scopus)

抄録

The growth behavior of anodic porous alumina formed by anodizing in novel electrolyte solutions, the cyclic oxocarbon acids croconic and rhodizonic acid, was investigated for the first time. High-purity aluminum specimens were anodized in 0.1 M croconic and rhodizonic acid solutions at various constant current densities. An anodic porous alumina film with a cell size of 200-450 nm grew uniformly on an aluminum substrate by rhodizonic acid anodizing at 5-40 A m -2 , and a black, burned oxide was formed at higher current density. The cell size of the porous alumina increased with current density and Corresponding anodizing voltage. Anodizing in croconic acid at 293 K caused the formation of thin anodic porous alumina films as well as black, thick burned oxides. The uniformity of the porous alumina improved by increasing the temperature of the croconic acid solution, and anodic porous alumina films with a uniform film thickness were successfully obtained. Our experimental results showed that the cyclic oxocarbon acids croconic and rhodizonic acid could be employed as a suitable electrolyte for the formation of anodic porous alumina films.

本文言語English
ページ(範囲)276-285
ページ数10
ジャーナルApplied Surface Science
313
DOI
出版ステータスPublished - 2014 9 15
外部発表はい

ASJC Scopus subject areas

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Fabrication of anodic porous alumina via anodizing in cyclic oxocarbon acids」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル