Fabrication and nanostructure of oriented FePt particles

Bo Bian, David E. Laughlin, Kazuhisa Sato, Yoshihiko Hirotsu

    研究成果: Conference article査読

    73 被引用数 (Scopus)

    抄録

    Thin films of oriented tetragonal FePt particles separated by amorphous alumina have been fabricated by electron beam evaporation. The ordering of the FePt particles without coarsening can be tailored by annealing conditions. The value of coercivity of the annealed film reached as high as 4.4 kOe. The perpendicular magnetic coercivity of the annealed film was slightly larger than in-plane coercivity. Some of the tetragonal FePt particles were found to have {111} twins and stacking faults. From our high-resolution electron microscopy observations, it was determined that central region of the ordered FePt particles tended to have oaxis perpendicular to the film plane.

    本文言語English
    ページ(範囲)6962-6964
    ページ数3
    ジャーナルJournal of Applied Physics
    87
    9 III
    DOI
    出版ステータスPublished - 2000 5 1
    イベント44th Annual Conference on Magnetism and Magnetic Materials - San Jose, CA, United States
    継続期間: 1999 11 151999 11 18

    ASJC Scopus subject areas

    • Physics and Astronomy(all)

    フィンガープリント 「Fabrication and nanostructure of oriented FePt particles」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル