Fabrication and mechanical properties of CeO2 stabilized tetragonal zirconia based nanocomposites incorporating Al2O3 dispersions

Masahiro Nawa, Syoichi Nakamoto, Keiichi Yamazaki, Tohru Sekino, Koichi Niihara

研究成果: Article査読

1 被引用数 (Scopus)

抄録

To compensate the definite disadvantages of ceria stabilized tetragonal zirconia polycrystal (Ce-TZP) as compared to Y-TZP ceramics, such as lower strength and lower hardness, we applied the idea of the nanocomposite to Ce-TZP/Al2O3 composite system. Zirconia matrix in these composites consisted of primarily the tetragonal phase and a small amount of the monoclinic phase. These composites partly possessed an intragranular nanostructure, in which fine alumina particles were trapped within the zirconia grains. At an optimum component for the 10Ce-TZP/30 vol% Al2O3 composite sintered at 1500°C, strength of 730 MPa and very high toughness of 10.2 Mpa·m1/2(SEPB) were achieved. This toughness value was in excess of that (8.1 MPa·m1/2) of WC/Co cermet. Therefore, it is suggested that this composite system would be expected as candidate for an attractive TZP ceramics, which have advantages of both high strength in Y-TZP and high toughness in Ce-TZP along with high resistance to low-temperature degradation.

本文言語English
ページ(範囲)415-420
ページ数6
ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
43
4
DOI
出版ステータスPublished - 1996 4

ASJC Scopus subject areas

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Fabrication and mechanical properties of CeO<sub>2</sub> stabilized tetragonal zirconia based nanocomposites incorporating Al<sub>2</sub>O<sub>3</sub> dispersions」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル