Experimental investigations of microstructures and phase equilibria in the Co-V-Ta ternary system

J. J. Ruan, C. P. Wang, S. Y. Yang, T. Omori, T. Yang, Y. Kimura, X. J. Liu, R. Kainuma, K. Ishida

研究成果: Article査読

11 被引用数 (Scopus)

抄録

The microstructures and the phase equilibria of the equilibrated Co-V-Ta ternary alloys have been investigated. Moreover, four isothermal sections of the Co-V-Ta ternary system at 1300, 1200, 1100 and 900°C are experimentally established. The corresponding results are summarized as follows: (1) the C14 phase with a large solubility of Co is observed both at 1300 and 1200°C, while it forms a ternary single phase region at 1100 and 900°C; (2) the C36 phase, containing a large solubility of V, is identified at 1300, 1200 and 1100°C, while it exists as a ternary single phase region at 900°C; (3) Co is in favor of stabilizing the C14 phase against lowerature, while V plays an analogous influence on the C36 phase; (4) the solubility of Ta in σ-Co2V3 phase decreases by a small amount as the temperature decreases from 1300 to 900°C. In addition, the experimental information obtained in the present work is not only essential for the thermodynamic assessment of the Co-V-Ta ternary system, but also important for the development of the Co-base alloys.

本文言語English
ページ(範囲)141-148
ページ数8
ジャーナルJournal of Alloys and Compounds
664
DOI
出版ステータスPublished - 2016 4 15

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Experimental investigations of microstructures and phase equilibria in the Co-V-Ta ternary system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル