Evolution of microstructure and mechanical properties of a 25Cr-20Ni heat resistant alloy after long-term service

Jingbo Yan, Yuefeng Gu, Fei Sun, Yaxin Xu, Yong Yuan, Jintao Lu, Zhen Yang, Yingying Dang

研究成果: Article

22 引用 (Scopus)

抜粋

This work investigated the effect of long-term service on the evolution of microstructure and properties of HR3C alloy. Its results show that large amount of discontinuous chromium carbide is accompanied by a chromium depletion area that is formed along the grain boundary. This depletion area promotes the crack nucleation and propagation at the carbide-matrix interface at the grain boundary, leading to a decrease in the alloy ductility at room temperature. However, this deteriorative effect is not obvious at high temperatures primarily because the fast drop of the grain strength. Therefore, the crack propagates easily across the grain during the alloy deformation at high temperatures.

元の言語English
ページ(範囲)289-298
ページ数10
ジャーナルMaterials Science and Engineering A
675
DOI
出版物ステータスPublished - 2016 10 15
外部発表Yes

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Evolution of microstructure and mechanical properties of a 25Cr-20Ni heat resistant alloy after long-term service' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用