Evaluation of thermal aging embrittlement in directionally solidified Ni-base superalloy by small punch test

Shin Ichi Komazaki, Tetsuo Shoji, Kazumune Takamura

研究成果: Article査読

7 被引用数 (Scopus)

抄録

In order to develop a procedure for evaluating the degradation of impact toughness in directionally solidified Ni-base superalloy CM247LC, which is commonly used for advanced gas turbine blades, the change in small punch (SP) fracture energy due to thermal aging has been investigated. The SP testing technique has been applied to materials aged under various aging conditions, and correlation with the results of Charpy V-notch impact tests has been examined. The experimental results reveal that SP fracture energy at room temperature decreases with aging at 800°C and is uniquely correlated with high-temperature Charpy impact toughness. The current experiment has shown that the SP testing technique is useful in evaluating the degree of thermal aging embrittlement, one of the parameters required for remaining-life prediction of aged components.

本文言語English
ページ(範囲)476-482
ページ数7
ジャーナルJournal of Engineering Materials and Technology, Transactions of the ASME
127
4
DOI
出版ステータスPublished - 2005 10 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Evaluation of thermal aging embrittlement in directionally solidified Ni-base superalloy by small punch test」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル