Epitaxial strain-controlled ionic conductivity in li-ion solid electrolyte Li0.33La0.56TiO3 thin films

Jie Wei, Daisuke Ogawa, Tomoteru Fukumura, Yasushi Hirose, Tetsuya Hasegawa

研究成果: Article査読

17 被引用数 (Scopus)

抄録

Ionic conductive Li0.33La0.56TiO3 (LLT) epitaxial thin films were grown on perovskite SrTiO3 (100), NdGaO3 (110), and (LaAlO3)0.3-(SrAl0.5Ta0.5O3)0.7 (100) single crystal substrates by pulsed laser deposition. The use of Li-rich Li0.84La0.56TiO3+δ target together with an optimized laser fluence resulted in the growth of phase pure LLT thin films with high growth rate of 2 nm/min. The a-axis and c-axis oriented films were selectively grown by choosing the substrates. Ionic conductivity at room temperature of LLT epitaxial film on NdGaO3 (110) substrate was close to that of bulk previously reported, representing the highly crystalline quality. In addition, the unequally strained lattice due to different in-plane lattice constants of orthorhombic NdGaO3 substrate resulted in laterally anisotropic ionic conductivity with different activation energy perpendicular to NdGaO3 [11¯0] and [001], 6.7 × 10-4 S·cm-1 with 0.34 eV and 4.3 × 10-4 S·cm-1 with 0.36 eV, respectively. This result suggests that the lattice engineering can provide a way to control Li ionic conduction.

本文言語English
ページ(範囲)2187-2191
ページ数5
ジャーナルCrystal Growth and Design
15
5
DOI
出版ステータスPublished - 2015 5 6
外部発表はい

ASJC Scopus subject areas

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics

フィンガープリント 「Epitaxial strain-controlled ionic conductivity in li-ion solid electrolyte Li<sub>0.33</sub>La<sub>0.56</sub>TiO<sub>3</sub> thin films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル