Enhancing Transport Performance in 7-filamentary Ba0.6K0.4Fe2As2 Wires and Tapes via Hot Isostatic Pressing

Shifa Liu, Chao Yao, He Huang, Chiheng Dong, Wenwen Guo, Zhe Cheng, Yanchang Zhu, Satoshi Awaji, Yanwei Ma

研究成果: Article査読

抄録

Iron-based superconductors (IBS) are considered as potential materials for manufacturing high-field magnets, for which developing multi-filamentary conductors with high performance and high strength is essential. Herein, 7-filamentary Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 (Ba122) round wires and tapes were successfully prepared through the ex situ powder-in-tube (PIT) method and treated by hot isostatic pressing (HIP) process. Pure Ba122 phase with roughly homogeneous element distribution was obtained in the superconducting filaments. The wires and tapes show very small low-temperature normal-state resistivity of 0.12 μΩ cm and 0.17 μΩ cm respectively owing to the high electrical conductivity of copper and silver. The HIP process greatly enhances the mass density of the superconducting filaments and promotes the formation of well-grown plate-like Ba122 grains. Vickers hardness measurements on the cross sections of these filaments reveal a rather good uniformity of the mass density. The transport critical current density (Jc) in the 7-filamentary Ba122/Ag/Cu round wires and tapes reached 1.3 × 104 A cm−2 and 4.8 × 104 A cm−2 at 4.2 K in 10 T respectively. These results indicate that hot isostatic pressing is advantageous in developing high-performance multi-filamentary iron-based superconductors.

本文言語English
論文番号1353870
ジャーナルPhysica C: Superconductivity and its applications
585
DOI
出版ステータスPublished - 2021 6 15

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Enhancing Transport Performance in 7-filamentary Ba<sub>0.6</sub>K<sub>0.4</sub>Fe<sub>2</sub>As<sub>2</sub> Wires and Tapes via Hot Isostatic Pressing」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル