Enhancement of nanovoid formation in annealed amorphous Al 2O3 including W

R. Nakamura, M. Ishimaru, A. Hirata, K. Sato, M. Tane, H. Kimizuka, T. Shudo, T. J. Konno, H. Nakajima

研究成果: Article査読

12 被引用数 (Scopus)

抄録

The effect of W on the nanovoid formation in annealed amorphous Al 2O3 was studied by transmission electron microscopy and molecular dynamics simulations. A comparison of the void formation behavior in electron-beam deposited Al2O3 (without W) and resistance-heating deposited Al2O3 (with 10 at. W) revealed that W enhances the formation and growth of nanovoids. An analysis of the pair distribution function (PDF) in both types of amorphous Al 2O3 showed that the introduction of W into amorphous Al2O3 brings about a significant change in the amorphous structure. Furthermore, it was found by high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) that sub-nm sized W clusters exist in as-deposited Al2O3 prepared by resistance-heating and then dissolve in the amorphous matrix with annealing. The combination of PDF analysis and HAADF-STEM observation provides evidence that the enhancement of void formation originates in the heterogeneous short-range atomic configurations induced by the addition of W.

本文言語English
論文番号064324
ジャーナルJournal of Applied Physics
110
6
DOI
出版ステータスPublished - 2011 9 15

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Enhancement of nanovoid formation in annealed amorphous Al <sub>2</sub>O<sub>3</sub> including W」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル