Electrical conductivity of dense nanocrystalline ceria under humidified atmosphere

Hitoshi Takamura, Naomi Takahashi

研究成果: Article査読

34 被引用数 (Scopus)

抄録

This paper describes the water adsorption behavior and electrical conductivity of Sm-doped ceria nanoparticles under humidified atmosphere. Single nano-sized 6 mol% Sm-doped ceria was prepared by either homogeneous precipitation using hexamethylenetetramine (HMTA) or ultraviolet (UV) laser irradiation. For the ceria nanoparticles prepared by HMTA, weakly-bundled agglomerates with pores were formed; as a result, approximately 3 mass% of water adsorption and capillary condensation were observed at room temperature. On the other hand, those prepared by UV laser irradiation formed tightly-bundled agglomerates without such pores; only 0.12 mass% of water was adsorbed under the same condition. For electrical conductivity measurements, dense samples having a relative density of 85 to 93% were prepared at 300 °C under 6 GPa by using a high-pressure apparatus. The proton conductivity of dense nanocrystalline ceria was on the order of 10- 7 to 10- 8 S/cm at around 50 °C under humidified atmosphere. As temperature increased, the proton conductivity decreased.

本文言語English
ページ(範囲)100-103
ページ数4
ジャーナルSolid State Ionics
181
3-4
DOI
出版ステータスPublished - 2010 2 24

ASJC Scopus subject areas

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics

フィンガープリント 「Electrical conductivity of dense nanocrystalline ceria under humidified atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル