Effects of silicon and manganese contents on V-bending in high-strength trip-aided dual-phase steel sheets with polygonal ferrite matrix

Akihiko Nagasaka, Tomohiko Hojo, Masaya Fujita, Takumi Ohashi, Mako Miyasaka, Yuki Shibayama, Eiji Akiyama

研究成果: Article査読

抄録

Effects of silicon and manganese contents on V-bending in high-strength TRIP-aided dual-phase (TDP) steel sheets with polygonal ferrite matrix were investigated for automotive applications. V-bending test was performed on a hydraulic testing machine at a processing speed of 1 mm/min, using a rectangular specimen (50 mm in length, 5 mm in width, 1.2 mm in thickness), 88-degree punch (2.0 mm in punch radius), and 88-degree die (12 mm in die width, 0.8 mm in die radius). The main results are as follows. (1) The 0.2C-(1.0–2.5)Si-(1.0–2.0)Mn, mass% TDP steel sheets were able to perform V-bending by strain-induced martensitic transformation of TRIP effect. On the other hand, ferrite-martensite dual-phase (MDP0) steel sheet of 900 MPa grade was not able to perform 90-degree V-bending because of initiation of crack on an outer surface. (2) The 0.2C- 2.5Si-1.5Mn, mass% TDP-G steel sheet of 980 MPa grade was able to enable the 90-degree V-bending that considered an amount of springback (Δθ = θ1 − θ2), in which the θ1 and the θ2 are a bending angle on loading and a bending angle after unloading respectively, of more than 2-degree by controlling a displacement of punch bottom dead center.

本文言語English
ページ(範囲)1980-1989
ページ数10
ジャーナルIsij International
61
6
DOI
出版ステータスPublished - 2021

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effects of silicon and manganese contents on V-bending in high-strength trip-aided dual-phase steel sheets with polygonal ferrite matrix」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル