Effects of Si and Cr on bainite microstructure of medium carbon steels

Takeshi Suzuki, Yoshiki Ono, Goro Miyamoto, Tadashi Furuhara

研究成果: Article査読

6 被引用数 (Scopus)

抄録

Effects of Si and Cr contents on bainite microstructure of medium carbon steels have been examined in order to obtain further information for good strength-ductility balanced spring steel. Four practical medium carbon steels, S55C, SUP9, SUP7 and SUP 12 were isothermally transformed at temperatures between 300°C and 500°C after austenitized at 1000°C. The microstructure was observed by means of scanning electron microscopy and transition electron microscopy. While carbide was found rapidly with bainite transformation in S55C without Si and Cr, carbide precipitation was suppressed by the increase of Si and Cr concentration in SUP9, SUP7 and SUP12. The fraction of retained austenite was increased with increasing of Si and Cr at the intermediate stage of bainite transformation because of the increase of C concentration in retained austenite. Particularly, Si addition promoted carbide-free bainitic ferrite and leading to larger amounts of retained austenite by carbon enrichment.

本文言語English
ページ(範囲)392-399
ページ数8
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
96
6
DOI
出版ステータスPublished - 2010

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effects of Si and Cr on bainite microstructure of medium carbon steels」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル