Effects of fine particle peening on fatigue strength of a TRIP-aided martensitic steel

Koh ichi Sugimoto, Yuta Mizuno, Masahiro Natori, Tomohiko Hojo

研究成果: Article査読

14 被引用数 (Scopus)

抄録

The effects of fine particle peening on the fatigue properties of a transformation-induced plasticity-aided martensitic steel with a chemical composition of 0.2% C, 1.5% Si, 1.5% Mn, 1.0% Cr, and 0.05% Nb (mass%) were investigated for applications in precision gears. When this steel was subjected to fine particle peening after heat treatment, higher fatigue limits and lower notch sensitivity were achieved compared with those of SNCM420 martensitic steel. The increased fatigue limits are principally associated with higher hardness and compressive residual stress on and just below the surface, as well as low surface roughness. Fine particle peening also increased the threshold stress intensity factor range in stage I, and decreased the crack propagation rate in stage II in this steel. The crack propagation behavior was mainly suppressed by (1) high hardness and high compressive residual stress, and (2) the strain-induced martensite transformation of retained austenite and high internal stress resulting from a difference in flow stress between the soft martensite matrix and the finely dispersed hard MA-like phase that developed during fatigue deformation.

本文言語English
ページ(範囲)206-214
ページ数9
ジャーナルInternational Journal of Fatigue
100
DOI
出版ステータスPublished - 2017 7 1

ASJC Scopus subject areas

  • モデリングとシミュレーション
  • 材料科学(全般)
  • 材料力学
  • 機械工学
  • 産業および生産工学

フィンガープリント

「Effects of fine particle peening on fatigue strength of a TRIP-aided martensitic steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル