Effects of 18MeV Fe8+ ion irradiation on superconductivity and microstructure of Bi2Sr2CaCu2Ox superconductor

Yukichi Sasaki, Weilie Zhou, Yuji Ishiguro, Yuichi Ikuhara

    研究成果: Article査読

    抄録

    Bi2Sr2CaCu2Ox single crystals were irradiated with 18MeV Fe8+ ion at room temperature. Superconductive property and microstructure of the samples after the irradiation were investigated by magnetization hysteresis (ΔM) and transmission electron microscopy (TEM). ΔM was enhanced by increasing ion dose up to 1 × 1012 ions/cm2, but decreased at the density of 1 × 1013 ions/cm2. The ion irradiation produced ellipse-like amorphous defects with the size of several nm, which may behave as flux pinning centers inside the crystals. The defects were formed in the band region of 0.5μm at the depth of about 4.5μm from the surface. The number of defects were equal to several times of applied ion dose. The optimum dose for improving superconductivity should be dominated by the defect size and spacing of defects to avoid overlapping among the defects.

    本文言語English
    ページ(範囲)197-200
    ページ数4
    ジャーナルJournal of the Ceramic Society of Japan. International ed.
    103
    2
    出版ステータスPublished - 1995 2月 1

    ASJC Scopus subject areas

    • 工学(全般)

    フィンガープリント

    「Effects of 18MeV Fe8+ ion irradiation on superconductivity and microstructure of Bi2Sr2CaCu2Ox superconductor」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル