Effect of Zr composition and heat-treatment on fracture toughness in Zr-Cu-Al bulk metallic glass

Nobuyuki Yoshida, Kazutaka Fujita, Yoshihiko Yokoyama, Hisamichi Kimura, Akihisa Inoue

研究成果: Article査読

20 被引用数 (Scopus)

抄録

Fracture toughness tests were carried out using different Zr composition in Zr-Cu-Al based bulk metallic glasses (BMGs) and heat-treated those just under the glass transition temperature (T g) in order to examine the effects of Zr composition and heat-treatment on the fracture toughness (K Q; fracture toughness including the values under unsatisfying the plane strain condition). Zr 50Cu 40Al 10, Zr 55Cu 35Al 10 and Zr 60Cu 30Al 10 BMGs fabricated by a tilt ark casting method were used. Heat-treatments were done for 90 minutes just under the T gs of each BMG. Tests were conducted based on ASTM E399. Compact type specimen was used (thickness = 2.3, 2.0 mm, thickness : width =1:4). Fatigue pre-crack was induced under ΔK less than 6 MPa ̇ m 1/2 by a servohydraulic fatigue machine and the fracture toughness test was done by using the same machine. The K Q dominantly increased with increasing the Zr composition. The K Q in heat-treated BMGs decreased in comparison with that in unheat-treated BMGs in all Zr composition. In the BMG of the high Zr composition, however, the decrease was small after heat-treatment, and the K Q showed enough high values. In heat-treated BMGs, the dispersion of K QS did not become small, but fatigue pre-cracks were induced more vertical against the loading axis and less bifurcation than those in unheat-treated BMGs.

本文言語English
ページ(範囲)730-735
ページ数6
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
71
9
DOI
出版ステータスPublished - 2007 9
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effect of Zr composition and heat-treatment on fracture toughness in Zr-Cu-Al bulk metallic glass」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル