Effect of weld thermal cycle, stress and helium content on helium bubble formation in stainless steels

S. Kawano, F. Kano, C. Kinoshita, A. Hasegawa, K. Abe

研究成果: Article査読

10 被引用数 (Scopus)

抄録

Helium bubble structure was examined on a helium-implanted stainless steel after applying thermal and stress cycle using a weld thermal and stress cycle simulator. Helium ions were implanted on Type 304 stainless steels up to 200 appm uniformly to a depth of 3.5 μm. The specimens were heated at various temperatures between 1073 and 1473 K for 2 s in Ar gas atmosphere. Tensile stresses from 0.5 to 8 MPa were applied during the thermal cycle. TEM observations revealed that size of the bubbles at grain boundaries was larger for the specimens with a higher tensile stress and with a higher annealing temperature. Densities of bubbles increased with increasing helium content. A theoretical model calculation showed a good agreement with the experimental results.

本文言語English
ページ(範囲)327-330
ページ数4
ジャーナルJournal of Nuclear Materials
307-311
1 SUPPL.
DOI
出版ステータスPublished - 2002 12 1

ASJC Scopus subject areas

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

フィンガープリント 「Effect of weld thermal cycle, stress and helium content on helium bubble formation in stainless steels」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル