Effect of ultrafine AlN/Al and Eu2O3 powder addition on sintering characteristics and thermal diffusivity of AlN

Xingguo Li, Katsuhisa Ohsaki, Masahiro Uda, Akihiko Chiba, Seiki Takahashi

研究成果: Article査読

抄録

The composite ultrafine powder AlN/Al with an average size of 300 nm was synthesized by arc-plasma method. This powder was added up to 15 mass% into the two kinds of commercial AlN powders prepared by the direct nitridation of Al and the carbon reduction nitriding of Al2O3. The mixed powders with the sintering aid Eu2O3 were sintered in the temperature range from 1923 to 2123 K in a flow of N2 gas and their density and thermal diffusivity were measured at 300 K. The composite ultrafine powder AlN/Al promotes the sintering of the two kinds of AlN powders. A sintered compact of AlN with the theoretical density was obtained at 1973 K by adjusting the amounts of Eu2O3 and composite ultrafine powder AlN/Al. The thermal diffusivity of the sintered sample increases with increasing the amount of the composite ultrafine powder AlN/Al if the sintering temperature is lower than 2073 K and the amount of Eu2O3 is less than 3 mass%. Otherwise it decreases with adding the composite ultrafine powder. Compared with the case used Y2O3 as the sintering aid, the effect for the composite ultrafine powder to promote the sintering of AlN is larger, but the effect for it to raise the thermal diffusivity of AlN is smaller when the sintering aid Eu2O3 is used.

本文言語English
ページ(範囲)99-104
ページ数6
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
61
2
DOI
出版ステータスPublished - 1997
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effect of ultrafine AlN/Al and Eu<sub>2</sub>O<sub>3</sub> powder addition on sintering characteristics and thermal diffusivity of AlN」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル