EFFECT OF THE NITROGEN ABSORPTION ON THE TEM STRUCTURE OF SUS304L AUSTENITIC STAINLESS STEEL WELD METAL.

Takeshi Kuwana, Hiroyuki Kokawa, Hiroshi Tsujii

研究成果: Article査読

11 被引用数 (Scopus)

抄録

The effect of the nitrogen absorption on the transmission electron microscopic structure of SUS304L austenitic stainless steel weld metal was investigated by varying the nitrogen partial pressure of the Ar-N//2 gas mixture welding atmosphere in an atmosphere-controlling chamber. An electron diffraction study suggested that the primary solidification mode of the weld metal alters from ferritic mode to austenitic one depending on the nitrogen partial pressure and the nitrogen content of weld metal. The austenite frequently takes a near Kurdjumov-Sachs orientation relationship with the adjacent primary ferrite, while the eutectic ferrite does not take the K-S one with the adjacent austenite. The amount of the eutectic ferrite phase increases with the nitrogen partial pressure and the nitrogen content. In the weld metal with no ferrite, precipitation on dislocations and grain boundaries was observed.

本文言語English
ページ(範囲)10-19
ページ数10
ジャーナルTransactions of the Japan Welding Society
17
1
出版ステータスPublished - 1986 4 1

ASJC Scopus subject areas

  • 工学(全般)

フィンガープリント

「EFFECT OF THE NITROGEN ABSORPTION ON THE TEM STRUCTURE OF SUS304L AUSTENITIC STAINLESS STEEL WELD METAL.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル