Effect of oxygen content and heat treatment on carbide precipitation behavior in PM Ni-base superalloys

Heng San Liu, Lin Zhang, Xin Bo He, Xuan Hui Qu, Hong Min Zhu, Guo Qing Zhang

研究成果: Article査読

9 被引用数 (Scopus)

抄録

The influence of oxygen content and heat treatment on the evolution of carbides in a powder metallurgy (PM) Ni-base superalloy was characterized. The results reveal that oxygen content has little influence on the precipitation of carbides inside the particles. However, under the consolidated state, stable Ti oxides on the particle surface act as nuclei for the precipitation of prior particle boundaries (PPB). Also, oxygen can diffuse internally along grain boundaries under compressive stress, which favors the precipitation of carbides inside the particles. Therefore, a higher amount of carbides will appear with more oxygen content in the case of consolidated alloys. It is also observed that PPB can be disrupted into discontinuous particles at 1200°C, but this carbide network is hard to be eliminated completely. The combined MC-M23C6 morphology approves the nucleation and growth mechanism of carbide evolution.

本文言語English
ページ(範囲)827-835
ページ数9
ジャーナルInternational Journal of Minerals, Metallurgy and Materials
19
9
DOI
出版ステータスPublished - 2012 9 1
外部発表はい

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Geochemistry and Petrology
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Effect of oxygen content and heat treatment on carbide precipitation behavior in PM Ni-base superalloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル