Effect of mechanical grinding under argon and hydrogen atmospheres on structural and hydriding properties of LaNi5

Shuko Munehiro, Keiji Fujii, Hironobu Fujii, Shin Ichi Orimo

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Effect of mechanical grinding (MG) under argon and hydrogen atmospheres on structural and hydriding properties were investigated in detail. In MG-LaNi5 under argon atmosphere, the grain size reaches approx. 20 nm for MG times of 60 min and almost remains unchanged for more longer MG times. The pressure-composition isotherm (P-C) in LaNi5 at room temperature indicates an enhancement of hydrogen solubility, a lowering of plateau pressure and a narrowing of width of plateau by MG like FeTi but not Mg2Ni. On the other hand, in reactive MG (RMG)-LaNi5 under hydrogen atmosphere, a nanocrystallized LaNi5H0.15 and amorphous phases coexist within 180 min of grinding time. For RMG times longer than 180 min, the nanostructured LaNi5H0.15 phase disappears and the remaining amorphous-LaNi5Hx dissociates into nano-Ni+LaNiyHz(y<5). The P-C isotherm indicates no-plateau in the LaNi5 produced by RMG longer than 60 min and the hydriding properties become worse and worse with increasing RMG times. From these results, we conclude that the hydriding properties could not be improved by structural modifications in the system containing metals with strong affinity for hydrogen like rare earth metals.

本文言語English
ページ(範囲)970-976
ページ数7
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
63
8
DOI
出版ステータスPublished - 1999 8月
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effect of mechanical grinding under argon and hydrogen atmospheres on structural and hydriding properties of LaNi5」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル