Effect of mechanical grinding under Ar and H 2 atmospheres on structural and hydriding properties in LaNi 5

H. Fujii, S. Munehiro, K. Fujii, S. Orimo

研究成果: Conference article

24 引用 (Scopus)

抜粋

The effects of mechanical grinding (MG) under argon and hydrogen gas atmospheres on the hydrogen storage properties of a LaNi 5 alloys were studied in detail. During MG under Ar atmosphere, a crystallite size reaches a ∼20 nm in grinding time of 60 min and reduces to approximately half this size after 600 min without any dissociation. The pressure-composition isotherm (P-C) in LaNi 5 at 293 K indicates an increase in hydrogen in zero offset region (trapping site region), a lowering of plateau pressure and a narrowing of the width of the pressure plateau by MG. On the other hand, in reactive MG (RMG)-LaNi 5 under H 2 atmosphere, a nanocrystalline LaNi 5H 0.15 and an amorphous phase coexist when the grinding time is less than 180 min. For much longer RMG times than 180 min, the nanostructured LaNi 5H 0.15 phase disappears and the remaining amorphous phase dissociates into nanocrystalline Ni+amorpous LaNi yH z (y<5). The P-C isotherm indicates no plateau for the LaNi 5 produced by RMG longer than 60 min and the hydriding properties become worse and worse with increasing RMG times. From the above results, we conclude that the hydriding properties cannot be improved by structural modifications in systems containing metals with a strong affinity for hydrogen like rare earth metals.

元の言語English
ページ(範囲)747-751
ページ数5
ジャーナルJournal of Alloys and Compounds
330-332
DOI
出版物ステータスPublished - 2002 1 17
外部発表Yes
イベントProceedings of the International Symposium on Metal-Hydrogen (MH 2000) - Noosa Heads, QLD, Australia
継続期間: 2000 10 12000 10 6

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Effect of mechanical grinding under Ar and H <sub>2</sub> atmospheres on structural and hydriding properties in LaNi <sub>5</sub>' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用