Effect of heat treatments on microstructure of rapidly solidified TiCo ribbons

Kyosuke Yoshimi, Akira Yamauchi, Ryusuke Nakamura, Sadahiro Tsurekawa, Shuji Hanada

研究成果: Conference article査読

1 被引用数 (Scopus)

抄録

The effect of heat treatments (aging or annealing) on microstructure was investigated for rapidly solidified ribbons of near-stoichiometric TiCo. In as-spun ribbons, it was observed by TEM that an equiaxed grain structure was developed and its crystal structure had been already B2-ordered, while a small amount of a second phase, Ti2Co, finely disperses in grains and along grain boundaries. Some grains were dislocation-free but others contained curved or helical dislocations and prismatic loops having a Burgers vector parallel to 〈100〉 directions. By annealing the as-spun ribbons at 700°C for 24h, the dislocation density was obviously increased compared with that of the as-spun ribbons, while grain growth appears to occur slightly. The increase of the dislocation density in the annealed ribbons is believed to result from the condensation and/or absorption of supersaturated vacancies. Therefore, the TEM observation results indicate that a large amount of supersaturated thermal vacancies were retained in the TiCo ribbons by the rapid solidification.

本文言語English
論文番号S1.5
ページ(範囲)449-454
ページ数6
ジャーナルMaterials Research Society Symposium Proceedings
842
出版ステータスPublished - 2005
イベント2004 MRS Fall Meeting - Boston, MA, United States
継続期間: 2004 11 292004 12 2

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Effect of heat treatments on microstructure of rapidly solidified TiCo ribbons」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル