Effect of Fe2+/T.Fe Ratio on the Dissolution Behavior of P from Steelmaking Slag with High P2O5 Content

Chuan ming Du, Xu Gao, Shigeru Ueda, Shin ya Kitamura

研究成果: Article査読

9 被引用数 (Scopus)

抄録

Steelmaking slag with high P2O5 content is generated when using high-P iron ores. This slag primarily consists of a CaO–SiO2–FeO–Fe2O3–P2O5 system and is regarded as a potential P source. To separate and recover P, selective leaching of the P-concentrated solid solution from steelmaking slag was employed. To determine the appropriate slag composition for selective leaching, it is necessary to clarify the influence of the molar ratio of Fe2+ to total Fe (Fe2+/T.Fe) on the dissolution behavior of steelmaking slag. This study found that as the Fe2+/T.Fe ratio in slag increased, the P2O5 content in the solid solution decreased, while the mass fraction of the solid solution increased; therefore, most of the P was still distributed in the solid solution. During leaching, citric acid showed an enhanced capacity to dissolve P from slag. When nitric acid is used as leaching agent, leaching should be conducted at a lower pH to achieve a leaching performance similar to that of citric acid. Because the presence of FeO in the solid solution deteriorated its dissolution, the dissolution ratio of P decreased significantly with the increasing Fe2+/T.Fe ratio in slag. By contrast, the dissolution of Fe was promoted. This was attributed to a higher dissolution of the CaO–SiO2–FeO matrix phase compared with the CaO–SiO2–Fe2O3 matrix phase. Therefore, to achieve a better selective leaching of P, steelmaking slag should be oxidized to lower the Fe2+/T.Fe ratio below 0.1.

本文言語English
ページ(範囲)443-454
ページ数12
ジャーナルJournal of Sustainable Metallurgy
4
4
DOI
出版ステータスPublished - 2018 12 1

ASJC Scopus subject areas

  • 環境科学(その他)
  • 材料力学
  • 金属および合金

フィンガープリント

「Effect of Fe<sup>2+</sup>/T.Fe Ratio on the Dissolution Behavior of P from Steelmaking Slag with High P<sub>2</sub>O<sub>5</sub> Content」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル