Effect of damage on fatigue crack growth rate under high-temperature creep-fatigue multiplication

Toshimitsu Yokobori, Yoshiyuki Kaji, Takashi Kuriyama, Takeo Yokobori

研究成果: Article

2 引用 (Scopus)

抜粋

The characterization for the crack growth rate and the progressive damage region around the crack tip of SUS 304 stainless steel were investigated with various holding times at the maximum stress in a trapozoidal wave in a vacuum at 680°C. From these experimental results, the crack growth rate approaches the creep crack growth rate, and the geometry of the progressive damage region around the crack tip becomes similar with the increase of stress holding time. The fracture surface shows integranular features dominated by creep in the case of with stress holding time, but does not show without stress holding time. This is distinguished from a triangular wave with no stress holding time, where the fracture implicitly involves fatigue and creep effects.

元の言語English
ページ(範囲)2349-2354
ページ数6
ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
57
発行部数542
出版物ステータスPublished - 1991 10
外部発表Yes

ASJC Scopus subject areas

  • Mechanical Engineering

フィンガープリント Effect of damage on fatigue crack growth rate under high-temperature creep-fatigue multiplication' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用