Effect of copper nanoparticle addition on the electrical and optical properties of thin films prepared from silver nanoparticles

Gang Qin, Lidan Fan, Akira Watanabe

研究成果: Article査読

7 被引用数 (Scopus)

抄録

The fabrication of transparent and conductive silver (Ag) and copper (Cu)-doped Ag films using simple spin-coating method with Ag and Cu nanoparticles (NPs) as starting material is described in this study. The aggregation of Ag NP and the grain formation caused by heat treatment were hindered by the addition of small amount Cu NP, and a continuous film was obtained even though the thickness was in the order of 10 nm. When the total metal concentration of NP solution precursor was 5 wt% with the ratio between Ag and Cu being 95:5, the surface resistivity (ρs) of Ag–Cu film was 3.17 Ω/sq; and when the concentration was reduced to 3.5 wt%, the ρs was 16.3 Ω/sq. The transmission of latter was more than 60 % with the maximum value 82.1 % at 328 nm in the near-UV region (300–400 nm), however, decreased to about 38 % in the visible region (400–700 nm) and near-IR region. The inhomogeneity of the film increased leading to the decrease of the conductivity with the time extension during the heat treatment.

本文言語English
ページ(範囲)49-56
ページ数8
ジャーナルJournal of Materials Science
50
1
DOI
出版ステータスPublished - 2015 1 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Effect of copper nanoparticle addition on the electrical and optical properties of thin films prepared from silver nanoparticles」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル