Effect of cerium and silicon additions to MCrAlY on the high-temperature oxidation behavior and bond strength of thermal barrier coatings

Masatoshi Tanno, Kazuhiro Ogawa, Tetsuo Shoji

研究成果: Conference article査読

7 被引用数 (Scopus)

抄録

It is well known, that thermally grown oxide (TGO) forms at the interface between the thermal barrier top coating (TBC) and the bond coating during service. In previous work, SEM images showed that the TOO layer contained at least two layers with different oxides. One layer was Al2O 3, and the other was a mixed oxide of NiO, CoO, Cr2O 3, and their spinels. It was supposed that a reason for macro-crack formation near an interface is due to a decrease in bond strength or to the formation of stress concentration sites caused by the formation of pores in the mixed oxide. In order to improve the bond strength, a modified bond coating material was developed, which is MCrAlY with Ce and Si added. Four -point bending tests were carried out to measure the bond strength of conventional TBC and of the modified TBC with MCrAlYCeSi bond coating. As a result, the TBC with modified bond coating had a bond strength superior to the conventional one. It is likely that the reason for the superior bond strength is due to a notable difference in oxidation behavior.

本文言語English
ページ(範囲)1061-1066
ページ数6
ジャーナルKey Engineering Materials
261-263
II
出版ステータスPublished - 2004 1月 1
イベントAdvances in Fracture and Failure Prevention: Proceedings of the Fifth International Conference on Fracture and Strength of Solids (FEOFS2003): Second International Conference on Physics and Chemistry of Fracture and Failure Prevention (2nd ICPCF) - Sendai, Japan
継続期間: 2003 10月 202003 10月 22

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Effect of cerium and silicon additions to MCrAlY on the high-temperature oxidation behavior and bond strength of thermal barrier coatings」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル