Effect of Al2O3 on high temperature mechanical properties of silicon nitride with Yb4Si2O7N2

Toshiyuki Nishimura, Mamoru Mitomo, Akira Ishida, Hidehiro Yoshida, Yuichi Ikuhara, Taketo Sakuma

    研究成果: Article査読

    2 被引用数 (Scopus)

    抄録

    Effect of Al2O3 on high temperature strength of silicon nitride with Yb4Si2O7N2 was investigated. A silicon nitride was fabricated by hot-pressing powder mixture including 87.4 mass% Si3N4, 12.1 mass% Yb2O3 and 0.5 mass% Al2O3. For reference, silicon nitride without Al2O3 addition was fabricated from powder mixture including 0.5 mass% SiO2 instead of Al2O3. Sinterability of silicon nitride with Al2O3 was higher than that of silicon nitride without Al2O3. Room temperature strength of the materials with Al2O3 was higher than that of the materials without Al2O3. Average strength at 1200 and 1350°C of both materials were almost same. The strength at 1500°C of the material with Al2O3 was slightly lower than that of the material without Al2O3. Creep resistance of the material with Al2O3 was lower than that of the materials without Al2O3.

    本文言語English
    ページ(範囲)801-804
    ページ数4
    ジャーナルJournal of the Ceramic Society of Japan
    105
    9
    DOI
    出版ステータスPublished - 1997 9月

    ASJC Scopus subject areas

    • セラミックおよび複合材料
    • 化学 (全般)
    • 凝縮系物理学
    • 材料化学

    フィンガープリント

    「Effect of Al2O3 on high temperature mechanical properties of silicon nitride with Yb4Si2O7N2」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル