Effect of additives (Alumina, Magnesia or Calcium fluoride) on dissolution rate of solid CaO into Calcium Silicate based slags

Fumiaki Kirihara, Sohei Sukenaga, Noritaka Saito, Kunihiko Nakashima

    研究成果: Article査読

    2 被引用数 (Scopus)

    抄録

    A study was undertaken to understand dissolution behavior of solid CaO particles into molten slags. Experiments were carried out to determine the effects of the basicity (CaO (mass%) / SiO2 (mass%)) and the kinds of additives (Al2O3, MgO or CaF2) on the dissolution rate of the rotating cylindrical CaO sinter into the ternary calcium silicate based slags at 1823 K. (Contact materials: graphite, Atmosphere: Ar) The dissolution rate increased with increasing rotation velocity of the cylindrical CaO sinter. It was found that the dissolution rate was highest with the CaO-SiO2-CaF2 slag so that CaF2 was proved as a good flux material. The dissolution rate of CaO increased with lowering slag basicity for the all slag system. However, this tendency was found to be weaker with the CaO-SiO2-Al2O3 system than the others due to the significant viscosity increase in the lower basicity region. The observation of the interface between CaO and each slag indicated that the dicalcium silicate (Ca2SiO4) phase was formed for all the slag systems. Further, the additive elements of Al and Mg were condensed in the interlayer between the Ca2SiO4 and the CaO phases as the calcium aluminates and the magnesia. On the other hand, in the case of fluorine containing system, solid phase precipitation was not observed in the interlayer. The results of CaO dissolution experiments indicated these interlayers also affected the dissolution rates. The CaO dissolution was retarded with the CaO-SiO2-MgO system, compared to the other two kinds of systems. It could be explained by the magnesia precipitation in the interlayer.

    本文言語English
    ページ(範囲)1361-1370
    ページ数10
    ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
    100
    11
    DOI
    出版ステータスPublished - 2014 1月 1

    ASJC Scopus subject areas

    • 凝縮系物理学
    • 物理化学および理論化学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Effect of additives (Alumina, Magnesia or Calcium fluoride) on dissolution rate of solid CaO into Calcium Silicate based slags」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル