Dissolution behavior of Mg from MgO–C refractory in Al-killed molten steel

Chunyang Liu, Xu Gao, Sun Joong Kim, Shigeru Ueda, Shin Ya Kitamura

研究成果: Review article査読

13 被引用数 (Scopus)


MgO–C refractory is a widely employed refractory in steel refining and it is considered as a Mg source to form MgO·Al2O3 spinel inclusions in steel melt. In this study, MgO–C refractories with various carbon contents were immersed into Al-killed molten steel to investigate the dissolution behavior of Mg from MgO–C refractory. The result showed that Mg gradually dissolved into the steel melt from the refractory, and spinel inclusions were formed. Al in the steel melt reduced MgO in the refractory and consequently, Mg was dissolved into the steel melt. The dissolved Mg increased with the Al content in the steel melt. Moreover, C in the MgO–C refractory also reduced MgO in the refractory and supplied Mg to the steel melt. However, when the C concentration in the refractory was lower than 10 mass%, Mg was not supplied. The reduction in MgO by Al and C occurred independently, and the Mg content in the steel was the sum of the Mg supplied by these reactions. In some regions at the refractory–steel melt interface, a spinel layer was observed; however, this layer was not formed uniformly.

ジャーナルIsij International
出版ステータスPublished - 2018

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Dissolution behavior of Mg from MgO–C refractory in Al-killed molten steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。