Dissolution behavior of Mg and Ca from dolomite refractory into Al-killed molten steel

Ying Ren, Chunyang Liu, Xu Gao, Lifeng Zhang, Shigeru Ueda, Shinya Kitamura

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Dolomite refractories are widely used in the refining process of clean steel and are considered potential sources of Mg and Ca that form MgO·Al2O3 spinel and CaO-containing inclusions. In this study, dolomite refractories were immersed into Al-killed molten steel with either 0.05% Al or 0.25% Al. The dissolution behavior of Mg and Ca from the dolomite refractory was studied, and the inclusion transformation behavior was observed. The results revealed that MgO in the dolomite refractory was reduced by Al in the molten steel, and the Mg content depended on the Al content. On the contrary, CaO barely dissolved into the molten steel even though the Al content increased. After immersion in both the low Al (0.05% Al) and high Al (0.25% Al) steels, an interfacial layer consisting of solid MgO and liquid phase CaO-Al2O3-MgO was formed on the surface of the rods. The initial Al2O3 inclusions gradually changed into Al2O3 saturated MgO-Al2O3 spinel after 60 min in low-Al steel; but were quickly transformed into MgO-saturated MgO-Al2O3 spinel in high Al steel. No CaO-containing inclusions were detected in the molten steel regardless of the immersion time and Al content.

本文言語English
ページ(範囲)2391-2399
ページ数9
ジャーナルIsij International
61
9
DOI
出版ステータスPublished - 2021

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Dissolution behavior of Mg and Ca from dolomite refractory into Al-killed molten steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル