Dislocation-free Czochralski Si crystal growth without a thin neck: Dislocation behavior due to incomplete seeding

Toshinori Taishi, Xinming Huang, Ichiro Yonenaga, Keigo Hoshikawa

研究成果: Article査読

15 被引用数 (Scopus)

抄録

Dislocation behavior at the interface between a heavily B-doped or B and Ge codoped Si seed and the grown crystal using Czochralski Si crystal growth under various seeding temperatures was investigated. When the diameter of the grown crystal just below the interface was larger than that of the seed, dislocation were generated in the grown crystal from the edge of the interface due to incomplete seeding. It was found that no dislocations were generated near the interface when the diameter was smaller than that of the seed, and the smaller diameter was simply realized by seeding at a higher temperature before pulling up the crystal. A practical industrial-scale dislocation-free Si crystal 8in in diameter was successfully grown without a thin neck by suppressing dislocations not only due to thermal shock and lattice misfit but also due to incomplete seeding.

本文言語English
ページ(範囲)58-64
ページ数7
ジャーナルJournal of Crystal Growth
258
1-2
DOI
出版ステータスPublished - 2003 10月
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 無機化学
  • 材料化学

フィンガープリント

「Dislocation-free Czochralski Si crystal growth without a thin neck: Dislocation behavior due to incomplete seeding」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル