Dielectric properties of poly- and single-crystalline BaTi 2O5

Rong Tu, Takashi Goto

研究成果: Article査読

29 被引用数 (Scopus)

抄録

Non-oriented and (010) oriented poly-crystalline BaTi2O 5 (BT2) was prepared by hot-pressing and arc-melting, respectively. The dielectric properties of poly-crystalline BT2 were compared with those of single-crystalline BT2 prepared by a floating zone method. The maximum permittivity of (010) oriented poly-crystalline BT 2 was 2000 at 720 K, whereas that of single-crystalline BT 2 was 6000 at the Curie temperature, Tc (750 K). The permittivity of non-oriented poly-crystalline BT2 was 30 to 300, having a small peak at 720 K. The tan δ of all specimens was 0.01 to 0.2 below Tc and significantly increased with increasing temperature above Tc. The electrical conductivity of (010) oriented poly- and single-crystalline BT2 had almost same values, which were one order higher than that of non-oriented poly-crystalline BT2 and (001) oriented single-crystalline BT2.

本文言語English
ページ(範囲)2898-2903
ページ数6
ジャーナルMaterials Transactions
47
12
DOI
出版ステータスPublished - 2006 12

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Dielectric properties of poly- and single-crystalline BaTi <sub>2</sub>O<sub>5</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル