Dielectric properties of (010) oriented polycrystalline Ta 2O5 substituted BaTi2O5 prepared by arc melting

Xin Yan Yue, Hong Tu, Takashi Goto

研究成果: Article査読

11 被引用数 (Scopus)


Ta2O5 substituted polycrystalline BaTi 2O5 (BT2T) was prepared from the raw materials of BaCO3, TiO2 and Ta2O5 by arc melting on a water-cooled copper plate in the nominal composition of Ba (Ti 1-1.25yTay)2O5 (y = 0 to 0.050). At y < 0.050, the main phase of the obtained specimens was BT2T which crystallized in a monoclinic cell with (010) orientation perpendicular to the copper plate. The a-axis length and ß angle increased from 1.6895 to 1.6916 nm and 103.11° to 103.20°, respectively, and then became almost constant with increasing y from 0 to 0.050. The b- and c-axes lengths were almost constant of 0.3934 and 0.9411 nm, respectively. A peak was observed in the temperature dependence of permittivity for all specimens. The Curie temperature shifted from 750 to 300 K with increasing y from 0 to 0.050. The permittivity of the specimen prepared at y= 0.0025 showed the highest value of 3800 at 707 K. Relaxor-like behaviors were observed for the specimens prepared at y> 0.025.

ジャーナルJournal of the Ceramic Society of Japan
出版ステータスPublished - 2008 3

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

フィンガープリント 「Dielectric properties of (010) oriented polycrystalline Ta <sub>2</sub>O<sub>5</sub> substituted BaTi<sub>2</sub>O<sub>5</sub> prepared by arc melting」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。