Desulfurization performance of sorbent derived from waste concrete

Atsushi Iizuka, Akihiro Yamasaki, Yukio Yanagisawa

    研究成果: Article査読

    4 被引用数 (Scopus)

    抄録

    This study examines the desulfurization performances of a sorbent derived from waste concrete through thermal gravimetric analysis in the temperature range from 303 to 1173 K. The sorbent is fine particles having a mean diameter distribution of 10-200 μm generated as a byproduct in a recycling process of aggregates from waste concrete. The sorbent is mainly composed of hydrated cement component, i.e. calcium silicate hydrate (C-S-H) and calcium hydroxide (Ca(OH)2). The sorbent showed SO2 removal activity over the temperature range studied. The desulfurization rate was lower under a lower temperature range up to 773 K, where the desulfurization rate gradually decreased with increasing temperature. The desulfurization activity at the lower temperatures can be attributed to the direct reaction of SO2 with C-S-H and Ca(OH)2. For the higher temperature range, the desulfurization rate was much higher, being almost half that for pure calcium carbonate, a conventional sorbent for dry desulfurization.

    本文言語English
    ページ(範囲)746-749
    ページ数4
    ジャーナルJournal of Chemical Engineering of Japan
    44
    10 SPEC. ISSUE
    DOI
    出版ステータスPublished - 2011 11 23

    ASJC Scopus subject areas

    • Chemical Engineering(all)
    • Chemistry(all)

    フィンガープリント 「Desulfurization performance of sorbent derived from waste concrete」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル