Deposition, structure and tribological behavior of silver-carbon nanocomposite coatings

Takanori Takeno, Hayato Saito, Minoru Goto, Julien Fontaine, Hiroyuki Miki, Michel Belin, Toshiyuki Takagi, Koshi Adachi

研究成果: Article査読

17 被引用数 (Scopus)

抄録

Silver-carbon nanocomposite coatings were deposited by plasma-enhanced chemical vapor deposition and d.c. magnetron sputtering of a silver target. Coatings with various metal concentrations were prepared by changing of acetylene and argon gas mixture ratio (C2H2/Ar), and concentrations of more than 40 at.%Ag was achieved in this study. Transmission electron microscope revealed that silver metallic grains with typically 15 nm were dispersed in amorphous carbon host matrix. Size of the grains increased with decrease of the gas mixture ratio due to secondary or triangularly formed metal grains. Tribological behavior of the coatings was investigated using reciprocating tribometer with in-situ electrical contact resistance measurement. Low and stable friction coefficient was achieved in the specimen with relatively low Ag concentration. Elemental mapping results on the ball after the friction tests reveal that tribofilm was formed on the ball when low and stable friction was achieved, and the tribofilm was mainly composed of C and Ag. It can be concluded that formation of the tribofilm is necessary for achieving low and stable friction.

本文言語English
ページ(範囲)20-26
ページ数7
ジャーナルDiamond and Related Materials
39
DOI
出版ステータスPublished - 2013

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Chemistry(all)
  • Mechanical Engineering
  • Materials Chemistry
  • Electrical and Electronic Engineering

フィンガープリント 「Deposition, structure and tribological behavior of silver-carbon nanocomposite coatings」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル