Dependence of crack growth kinetics on dendrite orientation and water chemistry for Alloy 182 weld metal in high-temperature water

Zhanpeng Lu, Junjie Chen, Tetsuo Shoji, Fanjiang Meng

研究成果: Article査読

9 被引用数 (Scopus)

抄録

Stress corrosion cracking growth rates of Alloy 182 weld metals in T-S and T-L orientations in 288 °C pure water with various dissolved oxygen and hydrogen concentrations were measured. Extensive inter-dendritic stress corrosion cracking paths on the side surfaces and fracture surfaces were observed. The crack growth path in the T-S orientation specimen was perpendicular to the applied loading direction, and parallel to the loading direction in the T-L specimen. Crack growth rates of the T-S specimen were significantly higher than those of the T-L specimen under the same test conditions. The crack growth rate decreased significantly with decreasing dissolved oxygen concentration. Adding dissolved hydrogen in water caused an apparent decrease of the alternating current potential drop signal during crack growth monitoring.

本文言語English
ページ(範囲)253-263
ページ数11
ジャーナルJournal of Nuclear Materials
458
DOI
出版ステータスPublished - 2015 3月

ASJC Scopus subject areas

  • 核物理学および高エネルギー物理学
  • 材料科学(全般)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「Dependence of crack growth kinetics on dendrite orientation and water chemistry for Alloy 182 weld metal in high-temperature water」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル