TY - JOUR
T1 - DENSITY AND ELECTRICAL CONDUCTIVITY OF NaF-AlF3 BINARY MELTS.
AU - Sato, Yuzuru
AU - Kojima, Akira
AU - Ejima, Tatsuhiko
N1 - Copyright:
Copyright 2017 Elsevier B.V., All rights reserved.
PY - 1977
Y1 - 1977
N2 - Densities and electrical conductivities of NaF-AlF//3 binary melts were measured over the composition range of 0-30 mol% AlF//3 and temperature range up to 1100 degree C. The density was determined by means of the Archimedian method with two sinkers of different size. For the electrical conductivity measurement, a specially designed conductivity cell made of boron nitride was used. The density shows a maximum at the composition of about 20 mol% AlF//3. On the other hand, the specific conductivity decreases steadily with increasing AlF//3 content.
AB - Densities and electrical conductivities of NaF-AlF//3 binary melts were measured over the composition range of 0-30 mol% AlF//3 and temperature range up to 1100 degree C. The density was determined by means of the Archimedian method with two sinkers of different size. For the electrical conductivity measurement, a specially designed conductivity cell made of boron nitride was used. The density shows a maximum at the composition of about 20 mol% AlF//3. On the other hand, the specific conductivity decreases steadily with increasing AlF//3 content.
UR - http://www.scopus.com/inward/record.url?scp=0017679961&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0017679961&partnerID=8YFLogxK
U2 - 10.2320/jinstmet1952.41.12_1249
DO - 10.2320/jinstmet1952.41.12_1249
M3 - Article
AN - SCOPUS:0017679961
SN - 0021-4876
VL - 41
SP - 1249
EP - 1256
JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
IS - 12
ER -