Densification and Structural Evolution in Spark Plasma Sintering Process of Mechanically Alloyed Nanocrystalline Fe-23Al-6C Powder

Yuichiro Koizumi, Takanori Tanaka, Yoritoshi Minamino, Nobuhiro Tsuji, Kiyoshi Mizuuchi, Yoshihira Ohkanda

研究成果: Article

10 引用 (Scopus)

抜粋

Nanocrystalline Fe-23 at%Al-6 at%C alloy powder was produced by mechanical alloying of the mixture of iron powder and aluminum powder (Fe-25 at%Al) with methanol, and was consolidated into fully dense compact by spark plasma sintering (SPS) at 1273 K. The compacts have nanocrystalline microstructure composed of mixture of α-phase grains and κ-carbide (Fe 3AlC) grains whose average grain size is about 50 nm. Although relatively large grains were also observed in places, their sizes were not over a few micrometers. The mechanisms of the densification and the structural evolution during the SPS process are discussed.

元の言語English
ページ(範囲)1604-1612
ページ数9
ジャーナルMaterials Transactions
44
発行部数8
DOI
出版物ステータスPublished - 2003 8

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Densification and Structural Evolution in Spark Plasma Sintering Process of Mechanically Alloyed Nanocrystalline Fe-23Al-6C Powder' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用