Dealloying behaviours of an equiatomic TiCu alloy

Zhenhua Dan, Fengxiang Qin, Yu Sugawara, Izumi Muto, Nobuyoshi Hara

研究成果: Article査読

6 被引用数 (Scopus)

抄録

The crystalline Ti50Cu50 ribbon was prepared by annealing its amorphous counterpart at 773 K, 84K higher than its crystallization temperature. An equiatomic TiCu intermetallic phase dominated in the matrix coexisting with trace Ti2Cu phase segregated on the grain boundary. A bi-continuous nanoporous copper from tenths of nanometers to hundredths of nanometers was obtained after dealloying the crystalline Ti 50Cu50 ribbons in 0.03 and 0.13 kmol/m3 HF solutions. The TiCu phase stayed inert at the initial immersion and the Ti 2Cu zone preferentially dissolved to form trenches. After a prolonged immersion in HF solutions, both TiCu and Ti2Cu phases were fully dealloyed. Final nanoporous Cu had a multiple-channel characteristic in different regions where various intermetallic phases distributed. Finer nanoporous Cu formed in the regions where the TiCu phase with a higher electrochemical stability dominated.

本文言語English
ページ(範囲)1120-1125
ページ数6
ジャーナルMaterials Transactions
54
7
DOI
出版ステータスPublished - 2013

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Dealloying behaviours of an equiatomic TiCu alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル