Crystallization behavior of Li 2O-SiO 2, Na 2O-SiO 2 and Na 2O-CaO-SiO 2 glasses

Koichi Tsutsumi, Jun Ichi Ohtake, Tetsuya Nagasaka, Mitsutaka Hino

研究成果: Article査読

2 被引用数 (Scopus)

抄録

It has been known that crystallization of mold powder is effective on the disturbance of heat transfer between mold and solidified shell in production of middle carbon steel slabs in continuous casting process. But it has not yet been made clear which composition of mold powder is the most suitable for crystallization. The crystallization behavior of Li 2O-SiO 2, Na 2O-SiO 2 and Na 2O-CaO-SiO 2 glasses was observed by differential thermal analysis (DTA) and hot-thermocouple methods with DTA in the present work. As a result, addition of alkaline metal and alkaline earth metal oxides to SiO 2 increased the critical cooling rate for glass formation in binary system of Li 2O-SiO 2 and Na 2O-SiO 2 ,and Li 2O-SiO 2 system crystallized easier than Na 2O-SiO 2 system. In ternary system of Na 2O-CaO-SiO 2, addition of Na 2O hurried the critical cooling rate at CaO/SiO 2 = 0.93 mass ratio, but the rate was almost constant in the composition range of more than 15 mass% Na 2O. The slag of CaO/SiO 2 = 0.93 made the rate faster than the slag of CaO/SiO 2 = 0.47 at constant content of 10mass% Na 2O.

本文言語English
ページ(範囲)66-71
ページ数6
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
84
6
出版ステータスPublished - 1998 12 1

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「Crystallization behavior of Li <sub>2</sub>O-SiO <sub>2</sub>, Na <sub>2</sub>O-SiO <sub>2</sub> and Na <sub>2</sub>O-CaO-SiO <sub>2</sub> glasses」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル