Crystal symmetry in single domains of PbZr0.54 Ti0.46 O3

Roland Schierholz, Hartmut Fuess, Kenji Tsuda, Yoishiro Ogata, Masami Terauchi, Ralf Theissmann

研究成果: Article

30 引用 (Scopus)

抜粋

This work focuses on the crystal symmetry of morphotropic PbZrx Ti1-x O3 (PZT). The crystal symmetry is investigated within single domains of ≈30-100nm width by convergent beam electron diffraction (CBED). The composition PbZr0.54 Ti0.46 O3 was chosen for experiments at room temperature and ≈300°C. The observed zone axis symmetry at room temperature was a (1̄ 10) mirror in some domains whereas symmetry was broken in neighboring domains. Therefore the highest crystal symmetry that can be attributed with certainty to the probed volume is monoclinic. The local symmetry of single cells might be lower due to disordered displacements of the cations. At ≈300°C the zone axis symmetry had changed to a (100) pc mirror that only occurs in the tetragonal phase of PZT.

元の言語English
記事番号024118
ジャーナルPhysical Review B - Condensed Matter and Materials Physics
78
発行部数2
DOI
出版物ステータスPublished - 2008 7 29

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

フィンガープリント Crystal symmetry in single domains of PbZr0.54 Ti0.46 O3' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用