Corrosion resistance and cracking susceptibility of 316L stainless steel in sulfuric acid-containing supercritical water

Yutaka Watanabe, Hiroshi Abe, Yuzo Daigo, Takashi Nishida

研究成果: Paper査読

1 被引用数 (Scopus)

抄録

Cracking susceptibility and characteristics were studied on non-sensitized UNS S31603 stainless steel by slow strain rate tests in supercritical and sub-critical water containing 0.01 mole/kg-H2SO4 at 400°C/25 MPa, 400°C/60 MPa, and 360°C/25 MPa with two levels of oxygen concentration, 8 and 800 ppm. The stainless steel had excellent corrosion resistance in 0.01 mole/kg-H2SO4 at 400°C when oxygen level was as high as 800 ppm and this was attributed to a thin and compact scale of Fe-Cr spinel and γ-Fe2O3 formed on the alloy. Cracking severity was higher for the supercritical conditions at 400°C than in the sub-critical water at 360°C. Although intergranular mode was dominant, a few traces of transgranular cracks were found in the less oxidizing 8 ppm O2 condition.

本文言語English
出版ステータスPublished - 2004 10 15
イベントCorrosion 2004 - New Orlean, LA, United States
継続期間: 2004 3 282004 4 1

Other

OtherCorrosion 2004
国/地域United States
CityNew Orlean, LA
Period04/3/2804/4/1

ASJC Scopus subject areas

  • エネルギー(全般)

フィンガープリント

「Corrosion resistance and cracking susceptibility of 316L stainless steel in sulfuric acid-containing supercritical water」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル