Corrosion characteristics of α-Ti and Ti2Cu composing Ti-Cu alloys

Yukyo Takada, Osamu Okuno

研究成果: Article査読

25 被引用数 (Scopus)

抄録

A series of binary Ti-Cu alloys containing 5-20 mass% Cu was prepared, and the corrosion behavior of α-Ti and Ti2Cu composing the Ti-Cu alloys were examined based on the anodic polarization curves and released ions in 0.9% NaCl and 1% lactic acid solutions. In both solutions, the Ti-Cu alloys showed the same anodic polarization curves as titanium in the condition below 1.4 V. However, precipitation of Ti2Cu contributed to a small increase in current densitiy in the transpassive region beyond 1.4 V. The amount of Cu ions released from Ti2Cu was 0.260 and 1.003 (μg/cm 2/7 days) in 0.9% NaCl and 1% lactic acid solutions respectively. Although these values were larger than those from α-Ti (0.0379 ± 0.0041 and 0.0962 ± 0.0327 (μg/cm2/7 days) in NaCl and lactic acid solutions respectively), they were not greater than those from type 4 gold alloy under the same conditions.

本文言語English
ページ(範囲)610-615
ページ数6
ジャーナルDental materials journal
24
4
DOI
出版ステータスPublished - 2005 12月

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 歯科学(全般)

フィンガープリント

「Corrosion characteristics of α-Ti and Ti2Cu composing Ti-Cu alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル