Continuous hydrothermal synthesis of ZnGa2O4:Mn 2+ nanoparticles at temperatures of 300-500 °c and pressures of 25-35 MPa

Hiromichi Hayashi, Atsuko Suino, Kenji Shimoyama, Masafumi Takesue, Suguru Tooyama, Richard L. Smith

研究成果: Article査読

8 被引用数 (Scopus)

抄録

Mn2+ doped ZnGa2O4 particles were continuously synthesized in subcritical and supercritical water using a flow hydrothermal reaction system. Zn, Ga and Mn nitrates were used as the starting materials. The syntheses were carried out at temperatures from 300 to 500 °C, at pressures from 25 to 35 MPa, at KOH concentration of 0.04 M, and for residence times from 0.13 to 1.13 s. X-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric differential thermal analysis (TG-DTA) and photoluminescent spectroscopy were used to characterize the samples. Single phase of ZnGa2O4 was achieved at residence times of less than 1 s. The crystallite sizes were in the range from 12 to 21 nm which tend to increase with an increase in the reaction temperature and with a decrease in the reaction pressure. Green emission was observed for the annealed samples under reducing conditions whereas as-synthesized samples did not exhibit photoluminescence.

本文言語English
ページ(範囲)1-6
ページ数6
ジャーナルJournal of Supercritical Fluids
77
DOI
出版ステータスPublished - 2013

ASJC Scopus subject areas

  • 化学工学(全般)
  • 凝縮系物理学
  • 物理化学および理論化学

フィンガープリント

「Continuous hydrothermal synthesis of ZnGa<sub>2</sub>O<sub>4</sub>:Mn <sup>2+</sup> nanoparticles at temperatures of 300-500 °c and pressures of 25-35 MPa」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル