Chemical diffusion in the iridium-rich A1 and L1 2 phases in the Ir-Nb system

Hiroshi Numakura, Tatsuru Watanabe, Makoto Uchida, Yoko Yamabe-Mitarai, Eisuke Bannai

研究成果: Article査読

2 被引用数 (Scopus)

抄録

The diffusion in iridium-rich Ir-Nh alloys has been studied by single-phase interdiffusion experiments. The chemical diffusion coefficient has been measured for the primary fee solid-solution and the L1 2 ordered compound Ir 3Nb in the temperature range between 1650 and 1950°C, using Ir/Ir-8Nb and Ir-26Nb/Ir-28Nb diffusion couples, respectively (numbers indicate mol%). While the chemical diffusion coefficient in the solid-solution phase is close to the tracer self-diffusion coefficient of pure iridium, the diffusion in the compound phase is extremely slow: the chemical diffusion coefficient is 1/40 to 1/50 of that in the solid solution. The low diffusion rate in the compound must be beneficial for high-temperature performance of refractory superalloys based on the Ir-Nb system.

本文言語English
ページ(範囲)638-643
ページ数6
ジャーナルJournal of Phase Equilibria and Diffusion
27
6
DOI
出版ステータスPublished - 2006 12

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Chemical diffusion in the iridium-rich A1 and L1 <sub>2</sub> phases in the Ir-Nb system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル